Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the js_composer domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /var/www/wp-includes/functions.php on line 6121

Notice: _load_textdomain_just_in_time تمّ استدعائه بشكل غير صحيح. Translation loading for the salient domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. من فضلك اطلع على تنقيح الأخطاء في ووردبريس لمزيد من المعلومات. (هذه الرسالة تمّت إضافتها في النسخة 6.7.0.) in /var/www/wp-includes/functions.php on line 6121
Forming & Blanking TC-358 Ar - V Steels Skip to main content

 التقطيع والتشكيل

TC-358

أداة فولاذية للعمل على البارد مناسبة لتصلب الأسطح وتشكيل قوالب لأغطية السيارات

لتركيب الكيميائي

NO DIN C Si Mn P S Cr Mo V
V’1.2358 60CrMoV18-5 0,58-0,62 0,20-0,50 0,70-0,90 Max 0,025 Max 0,05 4,30-4,70 0,40-0,60 0,20-0,30

خصائص المواد

  • متانة عالية
  • صلابة جيدة جدا
  • صلابة جيدة باللهب
  • قابلية جيدة للحام
  • سهولة الصيانة
  • التآلف الجيد
  • صلابة تصل إلى 58 HRc.
  • معالجة حرارية بسيطة
  • تشكيل سريع لصنع القوالب

التطبيقات

  • موت جسم السيارة
  • تشكيل القوالب
  • قوالب الرسم العميق
  • تقطيع وتشكيل الأجزاء
  • قوالب مجزأة
  • اللكمات مع الهندسة المعقدة
  • شفرات القص ولفائف منبسطه
  • شفرات القطع

المعالجة الحرارية

HEAT TREATMENT TEMPERATURE
Soft Annealing 820-860°C
Stress Relieving 600-650°C
Hardening 950-980°C

الخصائص الفيزيائية

20°C 100°C 200°C 300°C 400°C
Elastic Modulus [kN/mm²] 207 - - - -
Thermal Expansion Coefficient [10ˉ6/K] - 11,5 10,9 11,3 11,6
Thermal Conductivity [W/mK] 19,4 - 24,0 26,00 -

شروط التسليم

صلب ناعم 240 HB