Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the js_composer domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /var/www/wp-includes/functions.php on line 6121

Notice: _load_textdomain_just_in_time تمّ استدعائه بشكل غير صحيح. Translation loading for the salient domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. من فضلك اطلع على تنقيح الأخطاء في ووردبريس لمزيد من المعلومات. (هذه الرسالة تمّت إضافتها في النسخة 6.7.0.) in /var/www/wp-includes/functions.php on line 6121
Forming & Blanking 1.2767 Ar - V Steels Skip to main content

 التقطيع والتشكيل

V’1.2767

فولاذ أداة الكلمات الباردة مع صلابة جيدة جدًا بسبب المحتوى العالي من النيكل

التركيب الكيميائي

NO DIN C Si Mn Si Cr Mo Ni S P
V’1.2767 X45NiCrMo4 0,40-0,50 0,20-0,50 0,10-0,40 1,20-1,50 0,15-0,35 3,80-4,30 Max 0,05 Max 0,025

خصائص المواد

  • متانة جيدة جدا
  • آلية جيدة جدا
  • قابلية جيدة للتلميع
  • لا توجد قمه ثانوية في التخفيف
  • غير مناسب للطلاء

التطبيقات

  • سكاكين صناعية
  • شفرات المكابح ذات المقصلة والضغط
  • أدوات إعادة التدوير والسكاكين
  • قوالب السكاكين
  • قوالب العملات المعدنية
  • معدل تشوه عالي فى  صب القوالب على البارد
  • صناعة السحابات

المعالجة الحرارية

HEAT TREATMENT TEMPERATURE
Soft Annealing 600-650°C
Stress Relieving 600-650°C
Hardening 840-870°C
Tempering 150-600°C

الخصائص الفيزيائية

20°C 100°C 200°C 300°C 500°C
Elastic Modulus [kN/mm²] 215 - 198 - 179
Thermal Expansion Coefficient [10ˉ6/K] - 11,0 12,2 - 13,7
Thermal Conductivity [W/mK] 31 - 32,0 - 32,0

شروط التسليم

صلب ناعم 285 HB

الرسم البيانى