Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the js_composer domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /var/www/wp-includes/functions.php on line 6121

Notice: _load_textdomain_just_in_time تمّ استدعائه بشكل غير صحيح. Translation loading for the salient domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. من فضلك اطلع على تنقيح الأخطاء في ووردبريس لمزيد من المعلومات. (هذه الرسالة تمّت إضافتها في النسخة 6.7.0.) in /var/www/wp-includes/functions.php on line 6121
Aluminum Extrusion 1.2714 VEXtra Ar - V Steels Skip to main content

سحب الألمنيوم

1.2714 VEXtra

أداة عمل ساخنة مقاومة للتأثير لصقل المطرقة

التركيب الكيميائي

NO DIN C Si Mn P S Cr Mo V Ni
V’1.2714 55NiCrMoV 0,50-0,60 0,40-1,10 0,65-0,90 Max 0,025 Max 0,050 1,00-1,20 0,45-0,55 0,07-0,12 1,60-1,80

خصائص المواد

  • متانة ممتازة
  • ملف صلابة جيد جدا
  • ساعة  HRC  ميكنة جيدةلا يوصى باستخدامه في التطبيقات التي تزيد عن 44

التطبيقات

  • الكبس بالحدادة: قوالب صقل متوسطة وكبيرة الحجم
  • قلب وتجاويف لتزوير الضغط
  • دعم الأجزاء والحوامل في تشكيل القوالب
  • دعامات وكتل الدعم على قوالب الألمنيوم المصقولة

المعالجة الحرارية

HEAT TREATMENT TEMPERATURE
Soft Annealing 690-730°C
Stress Relieving 600-650°C
Hardening 860-900°C
Tempering 300-600°C

الخصائص الفيزيائية

20°C 100°C 200°C 400°C 600°C
Elastic Modulus [kN/mm²] 210 - - 198 178
Thermal Expansion Coefficient [10ˉ6/K] 12 12,1 13,1 13,5 14,3
Thermal Expansion [W/mK] 36,0 - 37,0 39,0 36,0
Toughness [J] 25,0 36,0 39,8 - -
Strength [N/mm²] 1150 - 1030 930 -

شروط التسليم

فقط المسطج والقوالب HRc مسبقة الصنع 40-44

صلب ناعم HB جولات فقط 250